Click image to view full size image
Submerged Welding Wire
The feature: excellent welding and mechanical performances,stable arc, easily removable residue,good seam forming and highly efficient deposition. Wire melting doesn’t lead to spashing or strong flashing. The seam surface is smooth and welding quality is guaranteed.
Specification:
Dia.2.0mm,2.5mm,3.2mm,4.0mm,5.0mm
Packing: 15-30kg/coil, then on pallet
Technical data:
Products | Chemical compositions of one sample wire (%) | Mechanical properties of one sample deposited metal | ||||||||||||
C | Mn | Si | Cr | Ni | Mo | Cu | Ti | S | P | Yield strength (Mpa) | Tensile Strength (Mpa) | Elongation (%) | Impact Energy (–20°C) (J) | |
H08A | 0.06 | 0.43 | 0.025 | 0.020 | 0.010 | - | 0.120 | - | 0.015 | 0.014 | 455 | 545 | 30 | 80 |
H08C | 0.07 | 0.41 | 0.027 | 0.019 | 0.017 | - | 0.120 | - | 0.012 | 0.011 | 460 | 555 | 31 | 87 |
H08E | 0.08 | 0.50 | 0.026 | 0.021 | 0.016 | - | 0.130 | - | 0.010 | 0.011 | 470 | 560 | 31 | 90 |
H08MnA | 0.06 | 0.94 | 0.024 | 0.025 | 0.015 | - | 0.130 | - | 0.014 | 0.017 | 469 | 578 | 28 | 87 |
H10Mn2 | 0.07 | 1.85 | 0.021 | 0.021 | 0.016 | - | 0.160 | - | 0.017 | 0.015 | 460 | 570 | 29 | 85 |
H10MnSi | 0.08 | 0.96 | 0.850 | 0.015 | 0.018 | - | 0.160 | - | 0.018 | 0.020 | 455 | 550 | 30 | 75 |
H08MnMoA | 0.08 | 1.45 | 0.180 | 0.018 | 0.015 | 0.38 | 0.150 | 0.12 | 0.020 | 0.019 | 490 | 650 | 27 | 85 |
H08Mn2MoA | 0.07 | 1.78 | 0.210 | 0.021 | 0.018 | 0.60 | 0.150 | 0.11 | 0.022 | 0.017 | 510 | 657 | 26 | 90 |
H08Mn2SiA | 0.07 | 1.85 | 0.750 | 0.015 | 0.018 | - | 0.150 | - | 0.018 | 0.020 | 455 | 560 | 27 | 89 |
Submerged Welding Wire and suitable Welding Flux